5454-H14 Aluminum plate sheet

5454-H14 aluminum refers to 5454 aluminum alloy that has been treated to H14 condition. Compared to other variants of 5454 aluminum, it has the lowest ductility.

5454-H14 aluminum refers to 5454 aluminum alloy that has been treated to H14 condition. In this state, the metal has achieved a balance of strength through strain hardening, between annealed (O) and fully hardened (H18) states. Compared to other variants of 5454 aluminum, 5454-H14 aluminum exhibits lower ductility but moderate strength, suitable for applications requiring higher hardness and moderate formability.

5454-H14 Aluminum plate sheet size

Alloy	Temper	Thickness	Width	Length
5454	H14	0.3-600	20-2650	500-16000

EN AW 5454 H14 Mechanical properties

Nominal thickness mm	Brinell hardness HBW	Yield strength R_{p0, 2} MPa min./max.	Tensile strength R_m MPa min./max.	Elongation A₅₀ _mm % min.	Elongation A % min.	Bending radius 180° t min.	Bending radius 90° t min.
0.2 - 0.5	81	220	270 - 325	2
0.5 - 1.5	81	220	270 - 325	3
1.5 - 3	81	220	270 - 325	3
3 - 6	81	220	270 - 325	4
6 - 12.5	81	220	270 - 325	5
12.5 - 25	81	220	270 - 325		4

5454 H14 Aluminum plate sheet chemical composition

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Standard
5454	0.25	0.40	0.10	0.50-1.0	2.4-3.0	0.05-0.20	0.25	0.20	EN573(WT%)

5454 H14 Aluminum Plate Sheet Related Questions

What is aluminum 5454 equivalent to?

UNS A95454, ISO AlMg3Mn, Aluminium 5454, AA5454, Al5454

What is 5454 aluminum grade?

5454 aluminum is a wrought aluminum-magnesium alloy known for its excellent corrosion resistance, suitable for marine environments and structural applications.

What is the difference between H14 and H32 aluminum?

H14 and H32 refer to different temper designations of aluminum alloys: H14 indicates strain-hardened and partially annealed condition, while H32 indicates strain-hardened and stabilized condition.

What is 3003 H14 aluminum?

3003 H14 aluminum is an alloy in which 3003 is the alloying element and H14 denotes the temper, indicating it has undergone strain-hardening and is partially annealed to achieve specified properties.

Products you may be interested in

Users viewing this material also viewed the following